ABSTRACT
Abstract This study evaluated the effect of toothbrushing on enamel-cementing material-ceramic bonded interfaces, using different cementing materials. Materials and Methods: Thirty enamel and thirty ceramic blocks were bonded with cementing materials to produce the samples that were bonded with three types of cementing materials: 1- RelyX Ultimate resin cement (REXU), 2- RelyX Unicem 2 self-adhesive resin cement (REU2) and 3- heated Z100 restorative composite (60°C). Bonded interfaces of the samples were toothbrushed and the surfaces of the 3 cementing materials were evaluated for roughness (RG, in µm), roughness profile (RP, in µm), and volume loss (VL, in µm3) (baseline and after 20,000 and 60,000 toothbrushing cycles). Data were evaluated by Generalized Linear Analysis (two factors: "material" and "toothbrushing cycle") and Bonferroni test (α=0.05). Results: REXU and Z100 exhibited lower RG than that presented by REU2, except after 60,000 toothbrushing cycles when only Z100 differed from REU2. The increase in toothbrushing cycles increased the RG and RP for all materials. REU2 also showed higher RP than those showed by REXU and Z100 when it was analyzed regarding the enamel. The VL of Z100 was the lowest with 20,000 toothbrushing cycles, regarding the enamel and ceramic. For 60,000 cycles, REXU showed the lowest VL regarding the ceramic, and REU2 had the highest VL regarding the enamel and ceramic. Conclusion: In general, REXU and Z100 showed the best results regarding the evaluations performed and the REU2 exhibited the highest RG, RP, and VL.
Resumo Este estudo avaliou o efeito da escovação nas interfaces de união esmalte-material cimentante-cerâmica, utilizando diferentes materiais cimentantes. Materiais e Métodos: Trinta esmaltes e trinta blocos cerâmicos foram unidos com materiais de cimentação para produzir as amostras que foram unidas com três tipos de materiais de cimentação: 1- cimento resinoso RelyX Ultimate (REXU), 2- cimento resinoso autoadesivo RelyX Unicem 2 (REU2) e 3-compósito restaurador aquecido Z100 (60°C). As interfaces coladas das amostras foram escovadas e as superfícies dos 3 materiais cimentantes foram avaliadas quanto à rugosidade (RG, em µm), perfil de rugosidade (RP, em µm) e perda de volume (VL, em µm3) (baseline e após 20.000 e 60.000 ciclos de escovação). Os dados foram avaliados por Análise Linear Generalizada (dois fatores: "material" e "ciclo de escovação") e teste de Bonferroni (α=0,05). Resultados: REXU e Z100 apresentaram menor RG do que REU2, exceto após 60.000 ciclos de escovação, quando Z100 diferiu apenas de REU2. O aumento dos ciclos de escovação aumentou o RG e RP para todos os materiais. O REU2 também apresentou PR maior que o REXU e Z100, quando analisado em relação ao esmalte. O VL de Z100 foi o menor com 20.000 ciclos de escovação em relação ao esmalte e cerâmica. Para 60.000 ciclos, o REXU apresentou o menor VL em relação à cerâmica e o REU2 o maior VL em relação ao esmalte e à cerâmica. Conclusão: De maneira geral, REXU e Z100 apresentaram os melhores resultados nas avaliações realizadas e o REU2 apresentou os maiores RG, RP e VL..
ABSTRACT
Abstract This in vitro study evaluated the effect of the beam homogeneity of a multiple-peak light-curing unit on the surface microhardness and the effect of toothbrushing wear on the microhardness, surface roughness, roughness profile, volume loss, and gloss retention of incremental and bulk-fill resin-based composites (RBCs). A LED light-curing unit (VALO) with four LEDs at the tip end (405, 445, 465A, and 465B nm emission peak) was used according to each manufacturer-recommended time to obtain disks (n=10) of six RBCs: Estelite Sigma Quick, Charisma Classic, Tetric EvoCeram Bulk Fill, Filtek Z250, Filtek Supreme Ultra, and Filtek Bulk Fill. Microhardness values were obtained according to each LED positioning of the light-curing unit on the top surface of the RBCs and were analyzed before and after toothbrushing regarding microhardness, surface roughness, roughness profile, volume loss, and gloss retention. Microhardness was considered homogeneous on the top surface regardless of the type of RBC or wavelength tested (p>0.05). Overall, toothbrushing did not reduce the microhardness of the RBCs but influenced the gloss values for most RBCs (p<0.001). Charisma Classic presented the greatest surface roughness and roughness profile after toothbrushing (p<0.05). Volume loss did not differ among RBCs (p>0.05). In conclusion, different wavelengths of the LED did not affect the top surface microhardness, regardless of the RBCs tested; and bulk-fill composites presented similar surface changes (microhardness, surface roughness, roughness profile, volume loss, and gloss retention) when compared to conventional composites after toothbrushing.
Resumo Este estudo in vitro avaliou a homogeneidade do feixe de um fotopolimerizador de múltiplos picos na microdureza superficial e o efeito da escovação na microdureza, rugosidade superficial, perfil de rugosidade, perda de volume e retenção do brilho de compósitos a base de resina (RBCs) incrementais ou bulk-fill. Um fotopolimerizador LED (VALO) com quatro LEDs na ponteira (405, 445, 465A e 465B nm de pico de emissão) foi usado de acordo com o tempo recomendado por cada fabricante para obtenção de discos (n=10) de seis RBCs: Estelite Sigma Quick, Charisma Classic, Tetric EvoCeram Bulk Fill, Filtek Z250, Filtek Supreme Ultra e Filtek Bulk Fill. Os valores de microdureza foram obtidos seguindo o posicionamento de cada LED na superfície superior das amostras e foram analisados antes e após a escovação quanto a microdureza, rugosidade superficial, perfil de rugosidade, perda de volume e retenção do brilho. A microdureza foi considerada homogênea no topo da superfície, independentemente do tipo de RBCs ou comprimento de onda testados (p>0.05). No geral, a escovação não reduziu a microdureza das RBCs, mas influenciou o brilho para a maioria das RBCs (p<0.001). Charisma Classic apresentou os maiores valores de rugosidade superficial e perfil de rugosidade após a escovação (p<0.05). A perda de volume não diferiu entre as RBCs (p>0.05). Em conclusão, os diferentes comprimentos de onda do LED não alteraram a microdureza do topo da superfície, independentemente das RBCs testadas; e as resinas bulk-fill apresentaram alterações superficiais similares (microdureza, rugosidade superficial, perfil de rugosidade, perda de volume e manutenção do brilho) quando comparadas às resinas convencionais após a escovação.